Technical Data

 

产品说明

 

Lustran ABS 556 resin is a low-gloss, medium-impact extrusion grade of ABS (acrylonitrile butadiene styrene). It has good melt strength for extrusion and thermoforming, and can be easily coextruded. It is easy to color with ABS color concentrates. The recommended ABS substrate is Lustran ABS 752 resin.

 

Lustran ABS 556 resin is used for low-gloss applications, such as motor vehicle dashboards, interior panels, and trim. This includes recreational vehicles, cars, trucks, heavy trucks, construction vehicles, forklift trucks, and farm equipment. As with any product, use of Lustran ABS 556 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E44741-235643

搜索 UL 黄卡 •  INEOS ABS (USA)

•  Lustran® ABS

供货地区 • 北美洲

特性 • 光泽，低 • 良好的着色性

• 良好的熔体强度 • 中等抗撞击性

用途 • 汽车领域的应用 • 汽车内部零件 • 汽车仪表板

机构评级 • EC 1907/2006 (REACH)

形式 • 粒子

加工方法 • 共挤出成型 • 片材挤出成型 • 热成型

 

物理性能 额定值单位制 测试方法

比重 1.06g/cm³ ASTM D792

特定体积 0.950cm³/g ASTM D792

熔流率（熔体流动速率） (230°C/10.0 kg) 10g/10 min ASTM D1238

机械性能 额定值单位制 测试方法

拉伸模量 1520MPa ASTM D638

抗张强度 ASTM D638

屈服 19.3MPa

断裂 22.1MPa

弯曲模量 1450MPa ASTM D790

弯曲强度 (屈服) 31.0MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 ASTM D256

-40°C, 3.18 mm 53J/m

-18°C, 3.18 mm 69J/m

23°C, 3.18 mm 110J/m

装有测量仪表的落镖冲击 4, 5 ASTM D3763

-34°C, Peak Energy 14.0J

-34°C, Total Energy 16.0J

-18°C, Peak Energy 19.0J

-18°C, Total Energy 23.0J

23°C, Total Energy 30.0J

23°C, Peak Energy 26.0J

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火 96.1°C

1.8 MPa, 未退火 86.1°C

线形热膨胀系数 - 流动 9.7E-5cm/cm/°C ASTM D696

RTI Elec (1.47 mm) 60.0°C UL 746

 

 

Lustran® ABS 556

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

热性能 额定值单位制 测试方法

RTI Imp (1.47 mm) 60.0°C UL 746

RTI (1.47 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

UL 阻燃等级 (1.47 mm) HB UL 94

光学性能 额定值单位制 测试方法

Gardner光泽度 (60°) < 10 ASTM D523

挤出 额定值单位制

干燥温度 82.2 到 93.3°C

干燥时间 3.0 到 4.0hr

建议的最大水分含量 < 0.030%

料筒1区温度 216 到 2560°C

料筒2区温度 216 到 241°C

料筒3区温度 216 到 241°C

料筒4区温度 216 到 241°C

料筒5区温度 216 到 241°C

熔体温度 216 到 249°C

口模温度 210 到 241°C

牵引辊 62.8 到 104°C

挤压说明

Compression Ratio: 2.5:1 to 2.7:1

Pump Ratio: 1.5 to 2.0

Max Regrind Allowed: 40%

 

 

 

 

 

 

 

 